Nylon CF (PA6-CF) is a carbon fiber reinforced polyamide offering exceptional stiffness, heat resistance, and dimensional stability. The carbon fiber reinforcement dramatically increases rigidity and thermal performance while reducing weight. Ideal for high-performance tooling, jigs, fixtures, and structural components. Requires a hardened steel nozzle.
Recommended Printing Settings
| Parameter | Value |
|---|---|
| Drying Settings (Blast Drying Oven) | 90 °C |
| Printing and Keeping Container's Humidity | < 15% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 280–290 °C: 40–60 mm/s | 290–310 °C: 60–100 mm/s |
| Bed Temperature | 100–110 °C |
| Printing Speed | 40–100 mm/s |
Physical Properties
| Property | Value |
|---|---|
| Density | 1.17 g/cm³ |
| Vicat Softening Temperature | 205 °C |
| Heat Deflection Temperature | 192 °C |
| Melting Temperature | 220 °C |
| Melt Index | 20 g/10 min |
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 100 MPa |
| Breaking Elongation Rate | 4.5 % |
| Flexural Strength | 135 MPa |
| Flexural Modulus | 6200 MPa |
| Impact Strength | 6.5 kJ/m² |
Disclaimer: The values presented in this document are typical and intended for reference purposes only. Actual results may vary depending on printing conditions, equipment, environment, and post-processing methods. A hardened steel nozzle is required for carbon fiber filaments. NE Solution recommends performing your own testing to validate suitability for your specific application.