Nylon PA6 is a high-performance engineering thermoplastic known for exceptional toughness, wear resistance, and chemical stability. It offers excellent layer adhesion and flexibility, making it ideal for functional parts, gears, hinges, and load-bearing components. Requires dry storage and enclosed printing for best results.
Recommended Printing Settings
| Parameter | Value |
|---|---|
| Drying Settings (Blast Drying Oven) | 90 °C |
| Printing and Keeping Container's Humidity | < 15% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 260–280 °C: 40–80 mm/s | 280–300 °C: 80–150 mm/s |
| Bed Temperature | 80–100 °C |
| Printing Speed | 40–150 mm/s |
Physical Properties
| Property | Value |
|---|---|
| Density | 1.14 g/cm³ |
| Vicat Softening Temperature | 180 °C |
| Heat Deflection Temperature | 80 °C |
| Melting Temperature | 220 °C |
| Melt Index | 18 g/10 min |
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 68 MPa |
| Breaking Elongation Rate | 30 % |
| Flexural Strength | 48 MPa |
| Flexural Modulus | 1700 MPa |
| Impact Strength | 5.5 kJ/m² |
Disclaimer: The values presented in this document are typical and intended for reference purposes only. Actual results may vary depending on printing conditions, equipment, environment, and post-processing methods. NE Solution recommends performing your own testing to validate suitability for your specific application.